Ceramic Ball

Silicon Nitride (Si3N4)

Zirconia (ZRO2)

Alumina(Al2O3)

Silicon carbide (SIC)

Ceramic balls are spherical, rolling elements that provide higher stiffness, lower thermal expansion, lighter weight, increased corrosion resistance, and higher electrical resistance than steel balls. They are made from a variety of ceramic materials.

LILY Bearing provide a wide range of ceramic ball options across a variety of sizes. Material options include Silicon nitride (Si3N4), Zirconia (ZRO2), Alumina (Al2O3) and Silicon carbide (SIC) from 0.4mm to just over 115mm in diameter with the most common sizes in between. Precision gradesprovided are 5, 10, 16, 25 and 100.

Different ceramic material have different properties, here is the introduction of ceramic materials and their properties.

Silicon Nitride Balls
Diameter	Grade	Maximum Temperature	Density	Hardness	Sphericity	Balls Qty/Kg
1/32″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995
1/16″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	149180
5/64″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995
3/32″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	44204
7/64″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995
1/8″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	18647
5/32″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	9547
3/16″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	5525
7/32″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	3480
15/64″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	2829
1/4″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	2331
17/64″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	1943
9/32″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	1637
5/16″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	1193
11/32″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	897
3/8″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	691
13/32″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995
13/31″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	543
7/16″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	435
29/64″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	392
15/32″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	354
31/64″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	320
1/2″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	291
17/32″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	243
9/16″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	205
19/32″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	174
5/8″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	149
21/32″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	129
11/16″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	112
23/32″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	98
3/4″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	86
25/32″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	76
13/16″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	68
7/8″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	54
29/32″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	49
15/16″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	44
1″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	36
1 1/16″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	30
1 1/8″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	26
19/16″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995
5/4″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995
1 3/8″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995
1 1/2″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995
1 5/8″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995
1 11/16″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995
1 7/8″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995
2″	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995
0.5mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995
0.7mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995
0.8mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995
1.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995
1.2mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	345389
1.3mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995
1.5mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	176839
2.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	74604
2.5mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	38197
3.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	22105
3.5mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	13920
4.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	9325
4.5mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	6550
5.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	4775
5.5mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	3587
6.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	2763
6.5mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	2173
7.0 mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	1740
7.5mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	1415
7.98mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995
8.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	1166
8.5mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	972
9.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	819
9.5mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	696
10.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	597
11.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	448
11.5mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	392
12.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	345
13.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	272
14.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	218
15.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	177
16.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	146
17.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	121
18.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	102
19.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	87
20.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	75
21.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	64
22.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	56
23.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	49
24.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	43
25.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	38
26.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	34
28.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	27
30.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995	22
35.0mm	10	800℃ \| 27040℉	3.20~3.30 g/cm3	75~80 HRC	0.999995
Zirconia Balls
Diameter	Grade	Maximum Temperature	Density	Hardness	Sphericity	Balls Qty/Kg
1/32″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995
1/16″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	79167
5/64″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995
3/32″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	23458
7/64″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995
1/8″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	9896
5/32″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	5066
3/16″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	2932
7/32″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	1847
15/64″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	1501
1/4″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	1237
17/64″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	1031
9/32″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	869
5/16″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	633
11/32″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	476
3/8″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	367
13/32″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995
13/31″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	288
7/16″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	231
29/64″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	208
15/32″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	188
31/64″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	170
1/2″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	155
17/32″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	129
9/16″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	109
19/32″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	92
5/8″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	79
21/32″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	68
11/16″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	59
23/32″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	52
3/4″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	46
25/32″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	41
13/16″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	36
7/8″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	29
29/32″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	26
15/16″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	23
1″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	19
1 1/16″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	16
1 1/8″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	14
19/16″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995
5/4″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995
1 3/8″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995
1 1/2″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995
1 5/8″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995
1 11/16″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995
1 7/8″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995
2″	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995
0.5mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995
0.7mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995
0.8mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995
1.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995
1.2mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	183291
1.3mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995
1.5mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	93845
2.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	39519
2.5mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	20270
3.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	11731
3.5mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	7387
4.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	4949
4.5mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	3476
5.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	2534
5.5mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	1904
6.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	1466
6.5mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	1153
7.0 mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	923
7.5mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	751
7.98mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995
8.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	619
8.5mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	516
9.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	434
9.5mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	369
10.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	317
11.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	238
11.5mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	208
12.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	183
13.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	144
14.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	115
15.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	94
16.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	77
17.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	64
18.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	54
19.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	46
20.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	40
21.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	34
22.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	30
23.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	26
24.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	23
25.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	20
26.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	18
28.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	14
30.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995	12
35.0mm	10	400℃ \| 13520℉	6.00 g/cm3	70 HRC	0.999995
Aluminum Oxide Balls
Diameter	Grade	Maximum Temperature	Density	Hardness	Sphericity	Balls Qty/Kg
1/32″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975
1/16″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	122404
5/64″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975
3/32″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	36270
7/64″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975
1/8″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	15301
5/32″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	7834
3/16″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	4533
7/32″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	2855
15/64″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	2321
1/4″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	1913
17/64″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	1594
9/32″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	1343
5/16″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	979
11/32″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	736
3/8″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	567
13/32″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975
13/31″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	446
7/16″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	357
29/64″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	321
15/32″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	290
31/64″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	263
1/2″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	239
17/32″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	199
9/16″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	168
19/32″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	143
5/8″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	122
21/32″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	106
11/16″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	92
23/32″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	80
3/4″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	71
25/32″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	63
13/16″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	56
7/8″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	45
29/32″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	40
15/16″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	36
1″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	30
1 1/16″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	25
1 1/8″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	21
19/16″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975
5/4″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975
1 3/8″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975
1 1/2″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975
1 5/8″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975
1 11/16″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975
1 7/8″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975
2″	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975
0.5mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975
0.7mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975
0.8mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975
1.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975
1.2mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	283396
1.3mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975
1.5mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	145099
2.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	61213
2.5mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	31341
3.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	18137
3.5mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	11422
4.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	7652
4.5mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	5374
5.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	3918
5.5mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	2943
6.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	2267
6.5mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	1783
7.0 mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	1428
7.5mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	1161
7.98mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975
8.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	956
8.5mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	797
9.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	672
9.5mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	571
10.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	490
11.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	368
11.5mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	322
12.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	283
13.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	223
14.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	178
15.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	145
16.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	120
17.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	100
18.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	84
19.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	71
20.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	61
21.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	53
22.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	46
23.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	40
24.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	35
25.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	31
26.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	28
28.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	22
30.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975	18
35.0mm	10	1000℃ \| 33800℉	3.95 g/cm3	80 HRC	0.999975
Silicon Carbide Balls
Diameter	Grade	Maximum Temperature	Density	Hardness	Sphericity	Balls Qty/Kg
Diameter	Grade	Maximum Temperature	Density	Hardness	Sphericity	Balls Qty/Kg
1/32″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995
1/16″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	151068
5/64″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995
3/32″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	44764
7/64″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995
1/8″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	18884
5/32″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	9668
3/16″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	5595
7/32″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	3524
15/64″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	2865
1/4″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	2360
17/64″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	1968
9/32″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	1658
5/16″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	1209
11/32″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	908
3/8″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	699
13/32″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995
13/31″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	550
7/16″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	440
29/64″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	396
15/32″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	358
31/64″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	325
1/2″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	295
17/32″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	246
9/16″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	207
19/32″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	176
5/8″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	151
21/32″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	130
11/16″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	113
23/32″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	99
3/4″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	87
25/32″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	77
13/16″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	69
7/8″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	55
29/32″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	50
15/16″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	45
1″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	37
1 1/16″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	31
1 1/8″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	26
19/16″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995
5/4″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995
1 3/8″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995
1 1/2″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995
1 5/8″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995
1 11/16″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995
1 7/8″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995
2″	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995
0.5mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995
0.7mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995
0.8mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995
1.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995
1.2mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	349761
1.3mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995
1.5mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	179077
2.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	75548
2.5mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	38681
3.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	22385
3.5mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	14096
4.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	9444
4.5mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	6632
5.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	4835
5.5mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	3633
6.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	2798
6.5mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	2201
7.0 mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	1762
7.5mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	1433
7.98mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995
8.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	1180
8.5mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	984
9.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	829
9.5mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	705
10.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	604
11.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	454
11.5mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	397
12.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	350
13.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	275
14.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	220
15.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	179
16.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	148
17.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	123
18.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	104
19.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	88
20.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	76
21.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	65
22.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	57
23.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	50
24.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	44
25.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	39
26.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	34
28.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	28
30.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995	22
35.0mm	10	1200℃ \| 40560℉	3.10 g/cm3	85~90 HRC	0.999995

Ceramic Ball

address

Yandian Industrial Park, Linqing City, Liaocheng City, Shandong Province, China

email

mike@machine-bearings.com

Quick Links

product